2.   GB  /  T  3620.2  chemical  composition  of    titanium  and  titanium  alloy  products  and  also  allowed  component  derivation

3.   GB  4698chemical  analysis  method  to  titanium  sponge,   titanium  and  titanium

1.   The  chemical  composition  of  titanium  and  titanium  alloy  rods  shall  be  meet  requirements  with  GB  /  T  3620.1,   the  chemical  composition  of  the  allowed  deviation  should  be  in  accordance  with  GB  /  T  3620.2  requirements,   by  reinspecting  of  demand-side.

2.   Diameter  or  side  lengths  and  the  allowed  deviation  of  hot  rods  should  be  in  accordance  with  the  requirements  of  Table  1.

3.   The  Diameter  of  the  rods  after  thermal  processing      and  been  processed  with  lathing,   (grinding)  and  cold-rolling,   its  deviation  should  be  allowed  to  table  II.

4.   The  non-roundness  of  the  rods  after  thermal  processing  (grinding)      should  be  less  than  the  half  of  its  dimension  tolerance.

5.   For  processing  the  Ti  rods  of  non  fixed  length  , the  length  300  ~  6000mm,   Length  at  annealing      state      300  ~  2000mm,   the  length  of  Constant  Length      or  double  length    should  under  the  rang  of  the  non-  fixed  dimension.       The  allowed  deviation  of  fixed  length  is  +  20  mm;   the  double  length  should  also  be  included  in  the  volume  of  incision  rods,   per  amount  of  incision  is  5mm.   the  fixed  length  or  double  length  should  be  specified  in  the  contract.

Table  I

Diameter  or  side  length

8~15

> 15~20

> 20~35

> 35~50

> 50~80

> 80~125

> 125~150

> 150~200

Hot  forging  bars

± 1.0

± 1.5

± 2.0

± 2.5

± 3.0

± 3.5

± 5.0

± 6.5

Hot  squeeze  bar

+0.8, -0.7

+0.8, -1.0

± 2.0

± 2.5

± 2.5

----

-----

----

Hot-rolled  bar

+0.6, -0.5

+0.7, -0.5

+1.2, -0.5

+1.5, -1.0

+2.0, -1.0

+2.2, -1.2